Can The Welding Scar On The Tempered Glass Be Removed?
Jun 02, 2017

Tempered glass is the ordinary annealing glass first cut into the required size, and then heated to close to the softening point of about 700 degrees, and then quickly and evenly cooled and get. After the steel treatment of the glass surface to form a uniform compressive stress, while the internal formation of tensile stress, so that the glass bending and impact strength can be improved, the strength of the tempered glass is about four times more than ordinary annealing glass.

Tempered glass to safety glass. Tempered glass is actually a kind of prestressed glass, in order to improve the strength of glass, the general use of chemical or physical methods, the composition of the glass surface compressive stress, the glass to withstand external forces when the primary side of the stress, and then forward the carrying capacity, enhance the glass itself Wind pressure, cold and heat, impact and so on.

The site in the welding when the welding slag dropped on the tempered glass, constitute a scar, then these in addition to the glass welding scar can also be removed?

In fact, there is no way to get rid of.

Over 300 degrees of temperature attached to the tempered glass surface, tempered glass is generally not damaged. The attachment of the glass surface can be removed with a gray knife, a knife and other things, but it will leave a trace of potholes.

Spot slag temperature generally more than 900 degrees, it is difficult to eradicate. Generally this happens only to replace the glass.

 Tempered quenching and cooling properties of tempered glass than ordinary glass has 3 to 5 times the increase, generally can withstand more than 250 degrees of temperature changes, to prevent the thermal cracking has a significant effect. Is a kind of safety glass. For the protection of high-rise buildings to provide qualified materials for security.